Welders Health: Side Effects of Galvanized Steel Welding
Welding galvanized steel is common in the metal fabricating industry. Most welders will at some point in their career perform a weld on galvanized steel and encounter galvanize poisoning or “metal fume fever.” Galvanize poisoning is a short-term reaction to overexposure of zinc oxide. Zinc oxide is produced when the steel’s galvanized coating is heated and evaporates.
What is Galvanized Steel
Galvanized steel is iron that is coated with zinc. When hot-dipped, the zinc chemically reacts with the base metal to form a corrosion resistant coating. The outer layer of the coating is pure zinc and subsequent layers gradually change in composition until they reach the iron base metal.
Between the zinc outer layer and iron base metal, zinc oxide is present in varying percentages of zinc to iron. The zinc oxide has the same chemical make-up as the white powder used by lifeguards to protect their noses against sunburn.
Signs of Galvanizing During Welding
Proper prep work to remove galvanizing from the weld area will reduce your exposure to zinc oxide fumes, but some galvanize will remain in the weld area. Yellowish-green smoke, white powdery particles floating in the air and white residue around the weld are sure signs that zinc oxide is present while welding.
Exposure to large amounts of the yellowish-green zinc oxide fumes will result in galvanize poisoning, commonly referred to as metal fume fever. The amount of exposure will have a direct effect on the severity of your symptoms.
Symptoms of Galvanize Poisoning (Metal Fume Fever)
Signs of galvanize poisoning are similar to flu symptoms. The onset of metal fume fever begins shortly after the body is exposed to zinc oxide and the symptoms include a slight headache and nausea. With increased exposure, flulike symptoms begin to set in.
Moderate zinc oxide exposure results in chills, shaking, slight fever, vomiting, and cold sweats. When the listed symptoms begin, it is time to stop welding and get fresh air. The symptoms can quickly become debilitating and you may need to go home and let the symptoms subside.
Fatalities have been associated with extreme cases of galvanize poisoning. Therefore when metal fume fever symptoms begin, you should immediately avoid further exposure.
How Long “Metal Fume Fever” Lasts
Metal fume fever is short-lived and the symptoms begin to fade within four hours of exposure and generally completely fade within 24 hours. Extreme cases of overexposure may see metal fume fever symptoms last for as long as 48 hours.
Drinking milk can quicken the recovery process as calcium helps remove the zinc build-up from your body.
There have been studies performed by the Centers for Disease Control (CDC) and the Occupational Safety and Health Administration (OSHA) on the long-term effects of welding galvanized steel. No studies have shown long-term health problems due to continued exposure to zinc oxide fumes or repeated cases of metal fume fever.
Avoiding Overexposure to Galvanize Fumes
Proper ventilation, avoiding direct contact with zinc oxide smoke, and proper pre-welding prep work will reduce the chances of your getting metal fume fever. Experienced welders that have had metal fume fever will tell you that drinking milk before, during and after welding galvanized steel will help eliminate the galvanize poisoning.
There are specialized fresh air welding hoods available for welders who frequently weld galvanized steel.
Was the article useful? Drop a comment and tell me what you think!
For vitamin/mineral/herbal supplements that are beneficial detoxifying the system and preventing metal poisoning in welders, I highly recommend Swissgarde South Africa’sNAFDAC approved Aloepower and Defender.
For orders or enquiries call 08060778264 , 08023467737 or visit :
- April 2017
- September 2015
- January 2014
- May 2013
- January 2013
- November 2012
- October 2012
- September 2012
- August 2012
- July 2012
- June 2012
- May 2012
- April 2012
- March 2012
- February 2012
- January 2012
- December 2011
- November 2011
- September 2011
- August 2011
- May 2011
- April 2011
- March 2011
- January 2011
- November 2010
- August 2010